Comparative first-principles study of TiN/SiN_x/TiN interfaces

Анотація

Using first-principles quantum molecular dynamics (QMD) calculations, heterostructures consisting of one monolayer of interfacial Si_xN_y inserted between several monolayers of thick slabs of B1(NaCl)-TiN (001) and (111) were investigated in the temperature range of 0 to 1400 K. For the interpretation of the interfacial structures, samples of amorphous SiN and Si₃N₄ were also generated. The temperature-dependent QMD calculations in combination with subsequent variable-cell structural relaxation revealed that the TiN(001)/B1-SiN/TiN(001) interface exists as a pseudomorphic B1-SiN layer only at 0 K. At finite temperature, this heterostructure transforms into distorted octahedral SiN₆ and tetrahedral SiN₄ units aligned along the {110} directions. At 300 K, the aggregates of the SiN_x units are close to a disordered, essentially amorphous SiN. After heating to 1400 K and subsequent relaxation at 300 K, the interfacial layer corresponds to a strongly distorted Si₃N₄-like structure. The B1-SiN, Si₃N₄-like SiN, and Si₃N₄-like Si₂N₃ interfaces between the TiN(111) slabs are stable in the whole temperature range considered here. The B1-SiN interfaces are unstable with respect to a formation of Si-vacancies at finite temperatures. An estimate of interfacial formation energies showed that the most favorable configurations of the (111) interfaces are silicon atoms tetrahedrally coordinated to nitrogen. The most stable (001) B1-derived heterostructure with Si_0.75N interface consists of both tetrahedrally and octahedrally coordinated silicon atoms. A comparison with the results obtained by earlier “static” ab initio calculations at 0 K shows the great advantage of the QMD calculations, which accounts for the effects of thermal activation of structural reconstructions.